Overview of materials for Polypropylene with 30% Mica Filler

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene with 30% Mica Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Mica Filler". Specific grades with primary filler content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.08 - 1.49 g/cc
0.0390 - 0.0538 lb/in³
Average value: 1.13 g/cc Grade Count:26
Filler Content 25.0 - 40.0 %
25.0 - 40.0 %
Average value: 27.3 % Grade Count:11
Water Absorption 0.0200 - 0.0300 %
0.0200 - 0.0300 %
Average value: 0.0267 % Grade Count:3
Linear Mold Shrinkage 0.00400 - 0.0130 cm/cm
0.00400 - 0.0130 in/in
Average value: 0.00840 cm/cm Grade Count:25
Melt Flow 4.00 - 20.0 g/10 min
4.00 - 20.0 g/10 min
Average value: 11.1 g/10 min Grade Count:16
Ash 30.0 %
30.0 %
Average value: 30.0 % Grade Count:9
Mechanical Properties Metric English Comments
Hardness, Rockwell R 30.0 - 98.0
30.0 - 98.0
Average value: 65.3 Grade Count:12
Hardness, Shore D 72.0 - 73.0
72.0 - 73.0
Average value: 72.4 Grade Count:5
Tensile Strength, Ultimate 14.0 - 33.8 MPa
2030 - 4900 psi
Average value: 26.2 MPa Grade Count:22
Tensile Strength, Yield 15.0 - 41.4 MPa
2180 - 6000 psi
Average value: 29.8 MPa Grade Count:13
Elongation at Break 2.50 - 15.0 %
2.50 - 15.0 %
Average value: 8.50 % Grade Count:19
Elongation at Yield 1.50 - 5.00 %
1.50 - 5.00 %
Average value: 3.19 % Grade Count:13
Modulus of Elasticity 2.00 - 6.21 GPa
290 - 900 ksi
Average value: 3.61 GPa Grade Count:14
Flexural Yield Strength 21.0 - 51.7 MPa
3050 - 7500 psi
Average value: 42.2 MPa Grade Count:17
Flexural Modulus 2.10 - 5.52 GPa
305 - 800 ksi
Average value: 3.31 GPa Grade Count:25
Izod Impact, Notched 0.214 - 1.49 J/cm
0.400 - 2.80 ft-lb/in
Average value: 0.523 J/cm Grade Count:25
Izod Impact, Unnotched 1.07 - 6.41 J/cm
2.00 - 12.0 ft-lb/in
Average value: 3.51 J/cm Grade Count:8
Gardner Impact 0.451 - 2.26 J
0.333 - 1.67 ft-lb
Average value: 1.13 J Grade Count:7
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 97.2 - 149 °C
207 - 300 °F
Average value: 122 °C Grade Count:21
Deflection Temperature at 1.8 MPa (264 psi) 55.0 - 130 °C
131 - 266 °F
Average value: 81.1 °C Grade Count:24
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:8
Processing Properties Metric English Comments
Nozzle Temperature 216 - 232 °C
420 - 450 °F
Average value: 222 °C Grade Count:5
Melt Temperature 191 - 243 °C
375 - 470 °F
Average value: 218 °C Grade Count:10
Mold Temperature 26.7 - 65.6 °C
80.0 - 150 °F
Average value: 43.4 °C Grade Count:10
Drying Temperature 65.6 - 90.0 °C
150 - 194 °F
Average value: 77.2 °C Grade Count:10
Moisture Content 0.0500 %
0.0500 %
Average value: 0.0500 % Grade Count:5
Injection Pressure 2.76 - 103 MPa
400 - 15000 psi
Average value: 41.9 MPa Grade Count:9