Overview of materials for Polysulfone, 10% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 10% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polysulfone, 10% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.27 - 1.49 g/cc
0.0459 - 0.0538 lb/in³
Average value: 1.34 g/cc Grade Count:14
Filler Content 5.00 - 10.0 %
5.00 - 10.0 %
Average value: 9.38 % Grade Count:8
Water Absorption 0.210 - 0.230 %
0.210 - 0.230 %
Average value: 0.223 % Grade Count:3
Linear Mold Shrinkage 0.00200 - 0.00700 cm/cm
0.00200 - 0.00700 in/in
Average value: 0.00429 cm/cm Grade Count:14
Melt Flow 6.50 g/10 min
6.50 g/10 min
Average value: 6.50 g/10 min Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122 - 123
122 - 123
Average value: 122 Grade Count:7
Tensile Strength, Ultimate 68.9 - 108 MPa
10000 - 15700 psi
Average value: 82.2 MPa Grade Count:13
Elongation at Break 2.00 - 8.00 %
2.00 - 8.00 %
Average value: 4.50 % Grade Count:14
Modulus of Elasticity 3.03 - 8.69 GPa
440 - 1260 ksi
Average value: 4.49 GPa Grade Count:13
Flexural Yield Strength 110 - 154 MPa
16000 - 22300 psi
Average value: 129 MPa Grade Count:14
Flexural Modulus 3.17 - 7.58 GPa
460 - 1100 ksi
Average value: 4.24 GPa Grade Count:14
Izod Impact, Notched 0.267 - 0.801 J/cm
0.500 - 1.50 ft-lb/in
Average value: 0.617 J/cm Grade Count:14
Izod Impact, Unnotched 3.74 - 13.3 J/cm
7.00 - 25.0 ft-lb/in
Average value: 6.86 J/cm Grade Count:10
Tensile Impact Strength 101 - 113 kJ/m²
48.1 - 53.8 ft-lb/in²
Average value: 108 kJ/m² Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 30.6 - 37.8 µm/m-°C
17.0 - 21.0 µin/in-°F
Average value: 35.4 µm/m-°C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 182 °C
360 °F
Average value: 182 °C Grade Count:7
Deflection Temperature at 1.8 MPa (264 psi) 174 - 183 °C
345 - 362 °F
Average value: 178 °C Grade Count:13
Flammability, UL94 HB - V-0
HB - V-0
Average value: 3.50 Grade Count:10
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 3.00e+16 ohm-cm
1000 - 3.00e+16 ohm-cm
Average value: 7.45e+15 ohm-cm Grade Count:11
Dielectric Constant 3.15 - 3.50
3.15 - 3.50
Average value: 3.37 Grade Count:6
Dielectric Strength 16.9 - 19.0 kV/mm
430 - 483 kV/in
Average value: 17.8 kV/mm Grade Count:7
Dissipation Factor 0.000700 - 0.00800
0.000700 - 0.00800
Average value: 0.00460 Grade Count:6
Arc Resistance 100 sec
100 sec
Average value: 100 sec Grade Count:3
Processing Properties Metric English Comments
Melt Temperature 332 - 399 °C
630 - 750 °F
Average value: 356 °C Grade Count:13
Mold Temperature 93.3 - 163 °C
200 - 325 °F
Average value: 126 °C Grade Count:13
Drying Temperature 135 - 191 °C
275 - 376 °F
Average value: 141 °C Grade Count:13
Moisture Content 0.150 %
0.150 %
Average value: 0.150 % Grade Count:10
Dew Point -31.7 °C
-25.0 °F
Average value: -31.7 °C Grade Count:10
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 96.5 MPa Grade Count:10