Overview of materials for Thermoset Polyurethane, Liquid

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Liquid
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Thermoset Polyurethane, Liquid.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.400 - 1.24 g/cc
0.0145 - 0.0448 lb/in³
Average value: 1.07 g/cc Grade Count:70
Water Absorption 0.300 - 4.00 %
0.300 - 4.00 %
Average value: 2.24 % Grade Count:7
Water Absorption at Saturation 0.300 - 4.00 %
0.300 - 4.00 %
Average value: 2.24 % Grade Count:7
Viscosity 90.0 - 100000 cP
90.0 - 100000 cP
Average value: 4830 cP Grade Count:41
100 - 15000 cP

@Temperature 45.0 - 82.2 °C
100 - 15000 cP

@Temperature 113 - 180 °F
Average value: 2520 cP Grade Count:8
Thickness 102 - 6100 microns
4.00 - 240 mil
Average value: 2320 microns Grade Count:6
Mechanical Properties Metric English Comments
Hardness, Shore A 20.0 - 95.0
20.0 - 95.0
Average value: 70.1 Grade Count:21
Hardness, Shore D 50.0 - 85.0
50.0 - 85.0
Average value: 69.4 Grade Count:9
Tensile Strength, Ultimate 0.586 - 55.2 MPa
85.0 - 8000 psi
Average value: 22.7 MPa Grade Count:36
Tensile Strength, Yield 0.165 - 89.0 MPa
24.0 - 12900 psi
Average value: 24.5 MPa Grade Count:15
Elongation at Break 3.50 - 900 %
3.50 - 900 %
Average value: 335 % Grade Count:37
Elongation at Yield 2.00 - 8.00 %
2.00 - 8.00 %
Average value: 4.33 % Grade Count:3
Modulus of Elasticity 0.440 - 3.20 GPa
63.8 - 464 ksi
Average value: 1.66 GPa Grade Count:10
Flexural Yield Strength 32.0 - 115 MPa
4640 - 16700 psi
Average value: 81.7 MPa Grade Count:5
Flexural Modulus 0.400 - 3.00 GPa
58.0 - 435 ksi
Average value: 2.19 GPa Grade Count:5
Rebound 5.00 - 65.0 %
5.00 - 65.0 %
Average value: 38.7 % Grade Count:13
Izod Impact, Notched 4.30 - 5.90 J/cm
8.06 - 11.1 ft-lb/in
Average value: 4.95 J/cm Grade Count:4
Charpy Impact Unnotched 0.900 J/cm² - NB
4.28 ft-lb/in² - NB
Average value: 3.52 J/cm² Grade Count:7
0.772 - 0.772 J/cm²

@Temperature -30.0 - -30.0 °C
3.67 - 3.67 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.772 J/cm² Grade Count:1
Charpy Impact, Notched 0.230 - 3.48 J/cm²
1.09 - 16.6 ft-lb/in²
Average value: 1.74 J/cm² Grade Count:3
Tear Strength 1.21 - 167 kN/m
6.90 - 950 pli
Average value: 52.9 kN/m Grade Count:26
Taber Abrasion, mg/1000 Cycles 3.00 - 1880
3.00 - 1880
Average value: 149 Grade Count:17
Thermal Properties Metric English Comments
CTE, linear 54.0 - 160 µm/m-°C
30.0 - 88.9 µin/in-°F
Average value: 105 µm/m-°C Grade Count:7
CTE, linear, Transverse to Flow 73.0 - 164 µm/m-°C
40.6 - 91.1 µin/in-°F
Average value: 120 µm/m-°C Grade Count:7
Deflection Temperature at 0.46 MPa (66 psi) 67.0 - 195 °C
153 - 383 °F
Average value: 142 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 54.0 - 136 °C
129 - 277 °F
Average value: 89.3 °C Grade Count:8
Vicat Softening Point 94.0 - 245 °C
201 - 473 °F
Average value: 163 °C Grade Count:4
Glass Transition Temp, Tg 83.0 - 145 °C
181 - 293 °F
Average value: 105 °C Grade Count:3
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 7.00e+13 - 1.00e+15 ohm-cm
7.00e+13 - 1.00e+15 ohm-cm
Average value: 4.88e+14 ohm-cm Grade Count:6
Surface Resistance 1.00e+13 - 2.00e+14 ohm
1.00e+13 - 2.00e+14 ohm
Average value: 5.67e+13 ohm Grade Count:6
Dielectric Strength 10.0 - 18.0 kV/mm
254 - 457 kV/in
Average value: 14.7 kV/mm Grade Count:6
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:5
Processing Properties Metric English Comments
Processing Temperature 18.3 - 93.3 °C
65.0 - 200 °F
Average value: 42.8 °C Grade Count:26
Mold Temperature 21.1 - 100 °C
70.0 - 212 °F
Average value: 59.6 °C Grade Count:26
Cure Time 5.00 - 30200 min
0.0833 - 504 hour
Average value: 2920 min Grade Count:19
15.0 - 1440 min

@Temperature 57.2 - 100 °C
0.250 - 24.0 hour

@Temperature 135 - 212 °F
Average value: 434 min Grade Count:17
Pot Life 0.750 - 60.0 min
0.750 - 60.0 min
Average value: 10.1 min Grade Count:28