- Owens Corning Glass Fiber Reinforced Polyester SMC (Compression), 22 wt.% glass
Owens Corning Glass Fiber Reinforced Polyester SMC (Compression), 22 wt.% glass
| Category | Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Owens Corning |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Owens Corning Glass Fiber Reinforced Polyester SMC (Compression), 22 wt.% glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyester thermosets are available in many formulations. They can be formulated for good to excellent resistance to acids, weak alkalis, and organic solvents. However, they are not recommended for use with strong alkalis. Data provided by the manufacturer, Owens Corning.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 68 | 68 | |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 0.50 % | 0.50 % | ASTM D638 |
| Modulus of Elasticity | 12.1 GPa | 1750 ksi | ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 10.9 GPa | 1580 ksi | ASTM D790 |
| Compressive Strength | 140 MPa | 20300 psi | ASTM D695 |
| Izod Impact, Notched | 2.27 J/cm | 4.25 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 °C |
6.60 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Specific Heat Capacity | 1.26 J/g-°C | 0.300 BTU/lb-°F | |
| Thermal Conductivity | 0.697 W/m-K | 4.84 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 5V |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.70e+15 ohm-cm | 2.70e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.2 @Frequency 60 Hz |
4.2 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 14.8 kV/mm | 375 kV/in | ASTM D149 |
| Arc Resistance | 190 sec | 190 sec | ASTM D495 |