Oxford Polymers C-Acetal 10MF-900 BK Acetal

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer Oxford Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers C-Acetal 10MF-900 BK Acetal.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Acetal Injection Molding Grade, 10 melt flow Processing and Delivery Form: Pellets and Injection MoldingSpecial Characteristics: Pre-colored blackInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D792
Water Absorption at Saturation 0.200 %
0.200 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0220 cm/cm

@Thickness 3.17 mm
0.0220 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.8 MPa
7800 psi
ASTM D638
Elongation at Break 10.0 %
10.0 %
ASTM D638
Flexural Strength 68.9 MPa
10000 psi
ASTM D790
Flexural Modulus 3.14 GPa
455 ksi
ASTM D790
Izod Impact, Notched 0.427 J/cm

@Thickness 3.17 mm
0.800 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 177 - 193 °C
350 - 380 °F
Middle Barrel Temperature 182 - 199 °C
360 - 390 °F
Front Barrel Temperature 188 - 204 °C
370 - 400 °F
Nozzle Temperature 188 - 204 °C
370 - 400 °F
Melt Temperature 182 - 218 °C
360 - 425 °F
Mold Temperature 79.4 - 107 °C
175 - 225 °F
Drying Temperature <= 93.3 °C
<= 200 °F
Dry Time 2.00 - 3.00 hour
2.00 - 3.00 hour