Oxford Polymers PEEK 20GF-Natural PEEK, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Oxford Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers PEEK 20GF-Natural PEEK, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Glass Fiber (20% Reinforced), PEEK, Polyetheretherketone injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Glass fiber Special Characteristics: Autoclavable, dimensional stability, high temp resistantInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
Water Absorption at Saturation 0.250 %
0.250 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00550 cm/cm

@Thickness 3.17 mm
0.00550 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23000 psi
ASTM D638
Elongation at Break 3.80 %
3.80 %
ASTM D638
Flexural Strength 239 MPa
34600 psi
ASTM D790
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D790
Izod Impact, Notched 1.49 J/cm

@Thickness 3.17 mm
2.80 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 343 °C
650 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 360 °C
680 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 374 °C
705 °F
Nozzle Temperature 379 °C
715 °F
Melt Temperature 363 °C
685 °F
Mold Temperature 177 °C
350 °F
Drying Temperature <= 149 °C
<= 300 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour