Oxford Polymers PEI -20GF-Natural PEI, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 20% Glass Fiber
Manufacturer Oxford Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers PEI -20GF-Natural PEI, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Glass Fiber (20% Reinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents Special Characteristics: Colors AvailableInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Water Absorption at Saturation 0.250 %
0.250 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00400 cm/cm

@Thickness 3.17 mm
0.00400 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 128.3 MPa
18610 psi
ASTM D638
Elongation at Break 2.50 %
2.50 %
ASTM D638
Flexural Strength 203 MPa
29500 psi
ASTM D790
Flexural Modulus 5.79 GPa
840 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
400 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 338 - 360 °C
640 - 680 °F
Middle Barrel Temperature 338 - 366 °C
640 - 690 °F
Front Barrel Temperature 343 - 371 °C
650 - 700 °F
Nozzle Temperature 343 - 371 °C
650 - 700 °F
Melt Temperature 349 - 371 °C
660 - 700 °F
Mold Temperature 65.6 - 177 °C
150 - 350 °F
Drying Temperature <= 135 °C
<= 275 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour