PTS PCA-2010 Flame Retardant PC/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS PCA-2010 Flame Retardant PC/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D1238
Melt Flow 22 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 22 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.1 MPa

@Thickness 3.17 mm
 9000 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 40 %

@Thickness 3.17 mm
 40 %

@Thickness 0.125 in
 ASTM D638
Flexural Strength 96.5 MPa

@Thickness 3.17 mm
 14000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.55 GPa

@Thickness 3.17 mm
 370 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 5.34 J/cm

@Thickness 3.17 mm
 10.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
ASTM D648
UL RTI, Electrical 60.0 °C
140 °F
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL RTI, Mechanical without Impact 60.0 °C
140 °F
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VB

@Thickness 3.00 mm
 5VB

@Thickness 0.118 in