PTS Trilac® ABS-HS4000 General Purpose ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trilac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® ABS-HS4000 General Purpose ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 2.59 GPa | 376 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Thickness 3.17 mm |
4.01 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V71H Fluoroelastomer Compound
- SABIC Innovative Plastics Cycoloy® CY6120 PC+ABS
- LNP Thermocomp® OF-1006 Polyphenylene Sulfide, Glass Fiber Reinforcement (discontinued **)
- Total 620 Polystyrene (discontinued **)
- Phillips 66 COPYLENE® CH050 Polypropylene, Homopolymer, Cast Film BOPP
- Spartech SparAlloy Rigid Foamed ABS Specialty Sheet
- Styron Pulse® 2200BG ABS + PC
- Solvay TECHNYL® 2912GMH7-P PA66, 63% glass fiber, DRY
- Total PPH 3576 H Polypropylene Homopolymer, Cast Film
- 3M 471+ Vinyl Tape
Copyright © lookpolymers.com All Rights Reserved