Material Notes:

TURBO SEAL SERIES 55 is a high performance anaerobic thread sealant designed for the locking and sealing of metal threaded pipes and fittings. The product cures quickly in the absence of air between close fitting surfaces and provides pressure resistance immediately after application. It is ideal to seal against gases, water, LPG, hydrocarbons, oils and other chemicals. Excellent thixotropic property prevents migration of the sealant before and during curingApplications:Ideal for locking and sealing of threaded metal pipes and fittings.Low viscosity with medium strength sealing properties.Part Numbers for this data: 55-050, 55-250Information provided by Palm Laboratories Adhesives

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc
Brookfield Viscosity	525 - 1850 cP	525 - 1850 cP	RVT Spindle 3 @ 20 rpm

Mechanical Properties	Metric	English	Comments
Shear Strength	>= 6.50 MPa	>= 943 psi	Steel Pins & Collars; ISO 10123

Thermal Properties	Metric	English	Comments
CTE, linear	0.800 µm/m-°C	0.444 µin/in-°F	ASTM D696
Specific Heat Capacity	0.300 J/g-°C	0.0717 BTU/lb-°F
Thermal Conductivity	0.100 W/m-K	0.694 BTU-in/hr-ft²-°F	ASTM C177
Flash Point	>= 37.8 °C	>= 100 °F

Processing Properties	Metric	English	Comments
Cure Time	120 - 240 min	2.00 - 4.00 hour	Functional
	1440 min	24.0 hour	Full
	10.0 - 30.0 min @Temperature -65.0 - 300 °C	0.167 - 0.500 hour @Temperature -85.0 - 572 °F	Handling

Descriptive Properties	Value	Comments
Appearance	Brown
Chemical Resistance	100% Initial Strength Retained	Ethanol at 22°C, at 500hrs
	100% Initial Strength Retained	Motor Oil at 125°C, at 500hrs
	100% Initial Strength Retained	Gasoline at 22°C, at 500hrs
	100% Initial Strength Retained	Brake Fluid at 22°C, at 500hrs
	100% Initial Strength Retained	Motor Oil at 125°C, at 1000hrs
	80% Initial Strength Retained	Acetone at 22°C, at 500hrs
	80% Initial Strength Retained	Acetone at 22°C, at 1000hrs
	90% Initial Strength Retained	Water/Glycol at 87°C, at 1000hrs
	90% Initial Strength Retained	Water/Glycol at 87°C, at 500hrs
	95% Initial Strength Retained	Gasoline at 22°C, at 1000hrs
	95% Initial Strength Retained	Brake Fluid at 22°C, at 1000hrs
	95% Initial Strength Retained	Ethanol at 22°C, at 1000hrs
Composition	Methacrylate ester
Torque	15 N.m	Breakaway, M10 steel nuts and bolts, ISO 10964
	25 N.m	Breakloose, pre-torqued to 5 N.m, M10 steel nuts and bolts, ISO 10964
	25 N.m	Max Prevail, pre-torqued to 5 N.m, M10 steel nuts and bolts N.m, ISO 10964
	9 N.m	Prevail, M10 steel nuts and bolts, ISO 10964