- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Park Electrochemical Corp. |
| Trade Name | Nelcote® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlled flow for ease of processingSelf adhesive for honeycomb or foam sandwich laminates without the use of film adhesiveFlexible cure temperature 180°F to 250°FGood electrical propertiesFlame and fire retardant per FAR 25.853Wet service temperatures up to 160°FApplications/Qualifications:RadomesAircraft InteriorsSecondary Aircraft StructuresSandwich PanelsMRI ResonatorsWidely specified on commercial and military aircraft programsInformation provided by Park Electrochemical Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Volatiles | <= 2.0 % @Temperature 135 °C |
<= 2.0 % @Temperature 275 °F |
8 min |
| Thickness | 178 microns | 7.00 mil | Per Ply |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 545 MPa @Temperature 93.3 °C |
79000 psi @Temperature 200 °F |
0° Direction, Dry; ASTM D638 |
| 565 MPa @Temperature 71.1 °C |
82000 psi @Temperature 160 °F |
0° Direction, Wet; ASTM D638 | |
| 593 MPa @Temperature 71.1 °C |
86000 psi @Temperature 160 °F |
0° Direction, Dry; ASTM D638 | |
| 621 MPa @Temperature 21.1 °C |
90000 psi @Temperature 70.0 °F |
0° Direction, Wet; ASTM D638 | |
| 648 MPa @Temperature 21.1 °C |
94000 psi @Temperature 70.0 °F |
0° Direction, Dry; ASTM D638 | |
| Tensile Modulus | 57.9 GPa @Temperature 71.1 °C |
8400 ksi @Temperature 160 °F |
0° Direction, Wet; ASTM D638 |
| 60.0 GPa @Temperature 71.1 °C |
8700 ksi @Temperature 160 °F |
0° Direction, Dry; ASTM D638 | |
| 60.0 GPa @Temperature 93.3 °C |
8700 ksi @Temperature 200 °F |
0° Direction, Dry; ASTM D638 | |
| 60.0 GPa @Temperature 21.1 °C |
8700 ksi @Temperature 70.0 °F |
0° Direction, Wet; ASTM D638 | |
| 60.7 GPa @Temperature 21.1 °C |
8800 ksi @Temperature 70.0 °F |
0° Direction, Dry; ASTM D638 | |
| Flexural Strength | 490 MPa @Temperature 71.1 °C |
71000 psi @Temperature 160 °F |
Wet; ASTM D790 |
| 545 MPa @Temperature 93.3 °C |
79000 psi @Temperature 200 °F |
Dry; ASTM D790 | |
| 579 MPa @Temperature 71.1 °C |
84000 psi @Temperature 160 °F |
Dry; ASTM D790 | |
| 689 MPa @Temperature 21.1 °C |
100000 psi @Temperature 70.0 °F |
Wet; ASTM D790 | |
| 745 MPa @Temperature 21.1 °C |
108000 psi @Temperature 70.0 °F |
Dry; ASTM D790 | |
| Flexural Modulus | 46.9 GPa @Temperature 71.1 °C |
6800 ksi @Temperature 160 °F |
Wet; ASTM D790 |
| 46.9 GPa @Temperature 71.1 °C |
6800 ksi @Temperature 160 °F |
Dry; ASTM D790 | |
| 47.6 GPa @Temperature 93.3 °C |
6900 ksi @Temperature 200 °F |
Dry; ASTM D790 | |
| 47.6 GPa @Temperature 21.1 °C |
6900 ksi @Temperature 70.0 °F |
Wet; ASTM D790 | |
| 49.6 GPa @Temperature 21.1 °C |
7200 ksi @Temperature 70.0 °F |
Dry; ASTM D790 | |
| Compressive Strength | 310 MPa @Temperature 71.1 °C |
45000 psi @Temperature 160 °F |
Wet; ASTM D695 |
| 310 MPa @Temperature 93.3 °C |
45000 psi @Temperature 200 °F |
Dry; ASTM D695 | |
| 352 MPa @Temperature 71.1 °C |
51000 psi @Temperature 160 °F |
Dry; ASTM D695 | |
| 400 MPa @Temperature 21.1 °C |
58000 psi @Temperature 70.0 °F |
Wet; ASTM D695 | |
| 427 MPa @Temperature 21.1 °C |
62000 psi @Temperature 70.0 °F |
Dry; ASTM D695 | |
| Compressive Modulus | 57.9 GPa @Temperature 21.1 °C |
8400 ksi @Temperature 70.0 °F |
Wet; ASTM D695 |
| 59.3 GPa @Temperature 71.1 °C |
8600 ksi @Temperature 160 °F |
Wet; ASTM D695 | |
| 59.3 GPa @Temperature 93.3 °C |
8600 ksi @Temperature 200 °F |
Dry; ASTM D695 | |
| 62.1 GPa @Temperature 21.1 °C |
9000 ksi @Temperature 70.0 °F |
Dry; ASTM D695 | |
| 67.6 GPa @Temperature 71.1 °C |
9800 ksi @Temperature 160 °F |
Dry; ASTM D695 | |
| Shear Strength | 30.3 MPa @Temperature 71.1 °C |
4400 psi @Temperature 160 °F |
Short-Beam, Wet; ASTM D2344 |
| 32.4 MPa @Temperature 93.3 °C |
4700 psi @Temperature 200 °F |
Short-Beam, Dry; ASTM D2344 | |
| 37.9 MPa @Temperature 71.1 °C |
5500 psi @Temperature 160 °F |
Short-Beam, Dry; ASTM D2344 | |
| 44.8 MPa @Temperature 21.1 °C |
6500 psi @Temperature 70.0 °F |
Short-Beam, Wet; ASTM D2344 | |
| 51.0 MPa @Temperature 21.1 °C |
7400 psi @Temperature 70.0 °F |
Short-Beam, Dry; ASTM D2344 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 115 °C | 239 °F | Dry; DMA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Gel Time | 6.00 min | 6.00 min | |
| Shelf Life | 12.0 Month @Temperature -17.8 °C |
12.0 Month @Temperature 0.000 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fabric Area Weight (g/m²) | 192.9 | |
| Prepreg Resin Content (%) | 42 | |
| Resin Flow (%) | 10 | 275°F, 50psi |