Parker Chomerics Tecknit Teckfip™ FIP-A Formed in Place Conductive Elastomer

Category	Polymer
Manufacturer	Parker Chomerics Tecknit
Trade Name	Teckfip™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Parker Chomerics Tecknit Teckfip™ FIP-A Formed in Place Conductive Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: This compound is ideally suited to corrosion-concerned applications where the gasket is applied to an aluminum casting. The corrosion resistance is enhanced due to the galvanic compatibility between the casting and the conductive Aluminum/Copper particle used. The compression set performance is good and this compound offers a very stable EMI shielding performance even under large mechanical stress. The electrical conductivity performance and EMI shielding is very similar to the high performing FIP-C elastomer gasket.Information provided by Chomerics

Physical Properties	Metric	English	Comments
Specific Gravity	2.975 - 4.025 g/cc	2.975 - 4.025 g/cc

Mechanical Properties	Metric	English
Hardness, Shore A	57 - 67	57 - 67
Tensile Strength	>= 0.621 MPa	>= 90.0 psi
Elongation at Break	>= 30 %	>= 30 %
Peel Strength	>= 9.00 kN/m	>= 51.4 pli
Compression Set	15 - 25 %	15 - 25 %
	15 % @Temperature 70.0 °C, Time 79200 sec	15 % @Temperature 158 °F, Time 22.0 hour

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	125 °C	257 °F
Minimum Service Temperature, Air	-55.0 °C	-67.0 °F

Electrical Properties	Metric	English
Volume Resistivity	<= 0.010 ohm-cm	<= 0.010 ohm-cm
Surface Resistance	<= 0.020 ohm	<= 0.020 ohm
	<= 0.020 ohm @Temperature 85.0 °C, Time 605000 sec	<= 0.020 ohm @Temperature 185 °F, Time 168 hour

Processing Properties	Metric	English	Comments
Dry Time	0.200 hour	0.200 hour	Tack Free
Cure Time	1440 min	24.0 hour
Shelf Life	1.00 Month	1.00 Month	Syringe
	6.00 Month	6.00 Month	Cartridge

Descriptive Properties	Value	Comments
Color	Silver/Tan
Filler	Silver Aluminum Heat Cure

Users viewing this material also viewed the following: