Pearl Engineering PEPLPET D-101-SH Monofilament Resin

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer Pearl Engineering Polymers Limited
Trade Name PEPLPET
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Pearl Engineering PEPLPET D-101-SH Monofilament Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Used in the paper industry as paper pulp nets.
Physical Properties Metric English Comments
Specific Gravity 1.38 - 1.42 g/cc
1.38 - 1.42 g/cc
PEPL-10-W-21
Bulk Density 0.800 g/cc
0.0289 lb/in³
PEPL-10-W-67
Bead Size 2.80 mm
0.110 in
chip size, length; PEPL-10-W-71
3.10 mm
0.122 in
chip size, D2; PEPL-10-W-71
3.80 mm
0.150 in
chip size, D1; PEPL-10-W-71
Viscosity Measurement 0.70 - 0.74
0.70 - 0.74
intrinsic, [dl/gm]; QCD--W1-42
Thermal Properties Metric English Comments
Heat of Fusion <= 65.0 J/g
<= 28.0 BTU/lb
Specific Heat Capacity 1.10 J/g-°C

@Temperature 20.0 °C
0.263 BTU/lb-°F

@Temperature 68.0 °F
1.37 J/g-°C

@Temperature 80.0 °C
0.327 BTU/lb-°F

@Temperature 176 °F
1.44 J/g-°C

@Temperature 100 °C
0.344 BTU/lb-°F

@Temperature 212 °F
1.82 J/g-°C

@Temperature 200 °C
0.435 BTU/lb-°F

@Temperature 392 °F
2.05 J/g-°C

@Temperature 280 °C
0.490 BTU/lb-°F

@Temperature 536 °F
Thermal Conductivity 0.213 W/m-K

@Temperature 280 °C
1.48 BTU-in/hr-ft²-°F

@Temperature 536 °F
liquid
0.242 W/m-K

@Temperature 20.0 °C
1.68 BTU-in/hr-ft²-°F

@Temperature 68.0 °F
solid
Melting Point 253 - 257 °C
487 - 495 °F
QCD--W1-49
Glass Transition Temp, Tg 77.0 - 81.0 °C
171 - 178 °F
QCD--W1-21
Flash Point 480 °C
896 °F
Processing Properties Metric English Comments
Moisture Content <= 0.20 %
<= 0.20 %
when packed; QCD--W1-54
Descriptive Properties Value Comments
Acetaldehydes (ppm) <1
QCD--W1-53
Chips per Gram 30-36
QCD--W1-47
COOH end groups (mval/kg) <15
QCD--W1-43
Fines (ppm) <100
QCD--W156