Permabond 2011 Cyanoacrylate, gel

Category Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer Permabond
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Permabond 2011 Cyanoacrylate, gel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and wood. Cyanoacrylate adhesives are single component adhesives that polymerize rapidly when pressed into a thin film between parts. The moisture adsorbed on the surface initiates the curing of the adhesive. Strong bonds are developed extremely fast and on a great variety of materials. These properties make PERMABOND cyanoacrylates the ideal adhesives for high speed production lines. Features & Benefits: Thixotropic Surface insensitive Fast cure Easy to apply and dispense High temperature resistance Maximum gap filling capability Information provided by Permabond.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
Uncured
1.10 g/cc
1.10 g/cc
Uncured
Viscosity 70 - 90 cP

@Temperature 25.0 °C
70 - 90 cP

@Temperature 77.0 °F
Uncured
Storage Temperature 2.00 - 7.00 °C
35.6 - 44.6 °F
2.00 - 7.00 °C
35.6 - 44.6 °F
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
ISO 868
85
85
ISO 868
Adhesive Bond Strength >= 2.00 MPa
>= 290 psi
Butyl Rubber, Substrate Failure, Shear; ISO 4587
>= 4.00 MPa
>= 580 psi
Nitrile Rubber, Substrate Failure, Shear; ISO 4587
>= 5.00 MPa
>= 725 psi
PC, Substrate Failure, Shear; ISO 4587
>= 6.00 MPa
>= 870 psi
ABS, Substrate Failure, Shear; ISO 4587
>= 6.00 MPa
>= 870 psi
PVC, Substrate Failure, Shear; ISO 4587
8.00 - 9.00 MPa
1160 - 1310 psi
Aluminum, Shear; ISO 4587
>= 9.00 MPa
>= 1310 psi
ABS, Substrate Failure, Shear; ISO 4587
>= 10.0 MPa
>= 1450 psi
Phenolic, Substrate Failure, Shear; ISO 4587
10.0 MPa
1450 psi
Zinc, Shear; ISO 4587
>= 14.0 MPa
>= 2030 psi
Acrylic, Shear; ISO 4587
14.0 MPa
2030 psi
Phenolic, Shear; ISO 4587
13.0 - 15.0 MPa
1890 - 2180 psi
Aluminum, Shear; ISO 4587
21.0 MPa
3050 psi
Brass, Shear; ISO 4587
21.0 MPa
3050 psi
Stainless Steel, Shear; ISO 4587
20.0 - 24.0 MPa
2900 - 3480 psi
Steel, Shear; ISO 4587
23.0 - 29.0 MPa
3340 - 4210 psi
Steel, Shear; ISO 4587
Impact 3.0 - 5.0
3.0 - 5.0
kJ/m<sup>2</sup> Adhesive Impact Strength; ASTM D950
3.0 - 5.0
3.0 - 5.0
kJ/m<sup>2</sup> Adhesive Impact Strength; ASTM D950
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
90.0 µm/m-°C
50.0 µin/in-°F
Thermal Conductivity 0.100 W/m-K
0.694 BTU-in/hr-ft²-°F
0.100 W/m-K
0.694 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 82.2 °C
180 °F
Minimum Service Temperature, Air -62.2 °C
-80.0 °F
Electrical Properties Metric English Comments
Dielectric Constant 2.5

@Frequency 10000 Hz
2.5

@Frequency 10000 Hz
2.5

@Frequency 10000 Hz
2.5

@Frequency 10000 Hz
Dielectric Strength 25.0 kV/mm
635 kV/in
25.0 kV/mm
635 kV/in
Processing Properties Metric English Comments
Cure Time 0.0833 - 0.167 min
0.00139 - 0.00278 hour
Steel, handling time
0.0833 - 0.167 min
0.00139 - 0.00278 hour
Buna N Rubber, handling time
0.0833 - 0.167 min
0.00139 - 0.00278 hour
Phenolic, handling time
0.167 - 0.250 min
0.00278 - 0.00417 hour
Steel, handling time
0.167 - 0.250 min
0.00278 - 0.00417 hour
Buna N Rubber, handling time
0.167 - 0.250 min
0.00278 - 0.00417 hour
Phenolic, handling time
1440 min
24.0 hour
full strength
1440 min
24.0 hour
full strength
Descriptive Properties Value Comments
Appearance Colorless
Uncured
Colorless Gel
Uncured
Maximum Gap Fill (mm) 0.15
0.5
Strength Retention 100% at 0°C
Relative to 0°C
100% at 0°C
Relative to 0°C
15% at 150°C
Relative to 0°C
15% at 150°C
Relative to 0°C
30% at 100°C
Relative to 0°C
50% at 100°C
Relative to 0°C
55% at -50°C
Relative to 0°C
75% at -50°C
Relative to 0°C
90% at 50°C
Relative to 0°C
90% at 50°C
Relative to 0°C