Perstorp Compounds AMITEC 751 Melamine
| Category | Polymer , Thermoset , Melamine , Melamine Formaldehyde, Molded, Unreinforced |
| Manufacturer | Perstorp Compounds |
| Trade Name | AMITEC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Perstorp Compounds AMITEC 751 Melamine.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Perstorp dinnerware compression and injection grade. Porcelain like properties suitable for household applications.Information provided by Perstorp Compounds Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | DIN 53 464 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 45.0 MPa | >= 6530 psi | ISO 178 |
| Flexural Strength | >= 80.0 MPa | >= 11600 psi | ISO 178 |
| Charpy Impact Unnotched | >= 0.500 J/cm² | >= 2.38 ft-lb/in² | 1eU; ISO 179 |
| Charpy Impact, Notched | >= 0.110 J/cm² | >= 0.524 ft-lb/in² | 1eU; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 155 °C | >= 311 °F | ISO 175 |
| Deflection Temperature at 8.0 MPa | >= 110 °C | >= 230 °F | ISO 175 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | >= 40 % | >= 40 % | ASTM D2863 |
| Shrinkage | 1.5 - 1.8 % | 1.5 - 1.8 % | Post Shrinkage; DIN 53 464 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm | DIN 53 482 |
| Dielectric Constant | 5.0 | 5.0 | DIN 53 483 |
| Comparative Tracking Index | >= 500 V | >= 500 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acetic Acid Fa Emission | >3 mg/l | DIN 7708 |
| Ethanol Fa Emission | >3 mg/l | DIN 7708 |
| Glow Bar 960°C 180 sec | passes | IEC 707 |
| H2O Fa Emission | >3 mg/l | DIN 7708 |
| Water Absorption [mg] | <200 | DIN 53 495/23°C 96h |
Users viewing this material also viewed the following:
- Momentive Performance Materials Silplusâ„¢ 70 MP Heat Cured Rubber
- H.C. Starck MoMP 4.5 - 5.5 micron Molybdenum Metal Powder, Mo (99.95%)
- Multibase Multi-Flex® A 5703 TPE Thermoplastic Elastomer
- Unipetrol PE HD LITEN® VL 10 HDPE
- Westlake EM800AA Low Density Polyethylene
- Williams Advanced Alloys WS199 Solder
- ExxonMobil Pax-Plus™ 3208 Blown Film Resin
- DuPont™ Surlyn® 1901 Sodium Ionomer Resin for Blown and Cast Film
- DuPont™ Surlyn® 1825 Zinc Ionomer
- Borealis Xmod™ GB306SAF Polypropylene, Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved