Phillips 66 COPYLENE® CH050 Polypropylene, Homopolymer, Cast Film BOPP

Category	Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Phillips 66
Trade Name	COPYLENE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Phillips 66 COPYLENE® CH050 Polypropylene, Homopolymer, Cast Film BOPP.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

COPYLENE™ CH050 is a polypropylene controlled rheology homopolymer resin designed for Cast Film BOPP (biaxially oriented polypropylene) film extrusion applications. Applications: Bags & Pouches, Peelable Film, Film Wrap, Food Packaging Film, Lamination Film, Twist Wrap Film, Surface Protection Film, Barrier Film. Equivalent to Pro-fax® HL457LInformation provided by Phillips 66.

Physical Properties	Metric	English	Comments
Density	0.902 g/cc	0.0326 lb/in³	ASTM D792
Melt Flow	5.0 g/10 min @Load 2.16 kg, Temperature 230 °C	5.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	33.8 MPa	4900 psi	2 in/min; ASTM D638
Elongation at Yield	12 %	12 %	ASTM D638
Flexural Modulus	1.34 GPa	195 ksi	0.05 in/min; 1% secant; Procedure A; ASTM D790
Izod Impact, Notched	0.374 J/cm @Temperature 23.0 °C	0.700 ft-lb/in @Temperature 73.4 °F	Method A; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	99.0 °C	210 °F	unannealed; ASTM D648

Descriptive Properties	Value	Comments
Process	Film