Phillips Sumika Marlex® CBF-300 Talc-Filled High Flow Thermoplastic Olefin (discontinued **)

Category	Polymer , Thermoplastic , Polyolefin
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Phillips Sumika Marlex® CBF-300 Talc-Filled High Flow Thermoplastic Olefin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Automotive exterior fasciasInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011. This product had been discontinued prior to the shutdown announcement.

Physical Properties	Metric	English	Comments
Density	1.02 g/cc @Thickness 3.17 mm	0.0368 lb/in³ @Thickness 0.125 in	injection molded specimen; ISO 1183
Melt Flow	30 g/10 min @Load 2.16 kg, Temperature 230 °C	30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60	15 second dwell; ISO 868
Tensile Strength, Yield	16.0 MPa @Thickness 3.17 mm	2320 psi @Thickness 0.125 in	50 mm/min, injection molded specimen; ISO 527
Flexural Modulus	1.25 GPa @Thickness 3.17 mm	181 ksi @Thickness 0.125 in	injection molded specimen, 2 mm/min; ISO 178
Izod Impact, Notched (ISO)	4.00 kJ/m² @Thickness 3.17 mm, Temperature -40.0 °C	1.90 ft-lb/in² @Thickness 0.125 in, Temperature -40.0 °F	ISO 180
	44.0 kJ/m² @Thickness 3.17 mm, Temperature 23.0 °C	20.9 ft-lb/in² @Thickness 0.125 in, Temperature 73.4 °F	ISO 180
Impact Test	17.0 J @Temperature 23.0 °C	12.5 ft-lb @Temperature 73.4 °F	Instrumented, 2.2 m/s, ductile; ASTM D3763
	24.0 J @Temperature -30.0 °C	17.7 ft-lb @Temperature -22.0 °F	Instrumented, 2.2 m/s, ductile; ASTM D3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	84.0 °C @Thickness 3.17 mm	183 °F @Thickness 0.125 in	injection molded specimen; ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	51.0 °C @Thickness 3.17 mm	124 °F @Thickness 0.125 in	injection molded specimen; ISO 75