Plaslok 201 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Woodflour/Mineral Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plaslok 201 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 201 is a two-stage, woodflour and mineral-filled phenolic molding compound formulated to have an excellent balance of molded properties. The material provides good electrical insulation values and physical properties combined with versatile molding characteristics.Data provided by Plaslok Corporation.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ASTM D792
Apparent Bulk Density 0.600 g/cc
0.0217 lb/in³
ASTM D1895
Water Absorption 0.45 %
0.45 %
ASTM D570
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Compression; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 52.0 MPa
7540 psi
ASTM D638
Flexural Yield Strength 76.0 MPa
11000 psi
ASTM D790
Flexural Modulus 6.90 GPa
1000 ksi
ASTM D790
Compressive Yield Strength 228 MPa
33100 psi
ASTM D695
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 168 °C
334 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.47 mm
302 °F

@Thickness 0.0579 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.47 mm
302 °F

@Thickness 0.0579 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.47 mm
302 °F

@Thickness 0.0579 in
Flammability, UL94 HB
HB
3.05mm
HB
HB
3.05mm
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 5.8
5.8
60 Hz; ASTM D150
5.8
5.8
60 Hz; ASTM D150
Dielectric Strength 14.2 kV/mm
361 kV/in
ASTM D149
Dissipation Factor 0.030
0.030
1 MHz; ASTM D150
0.060
0.060
60 Hz; ASTM D150
Comparative Tracking Index 140 V
140 V
UL 746