- Plastcom SLOVALEN PC 78 FRD 3 Polypropylene Copolymer, Halogen Flame Retardant
Plastcom SLOVALEN PC 78 FRD 3 Polypropylene Copolymer, Halogen Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Flame Retardant |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVALEN PC 78 FRD 3 Polypropylene Copolymer, Halogen Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FeaturesDetermined for environment where contact with water is possible because the electric properties do not change by conditioning. Application - terminals, coil forms, guides in washing machines, tea-pots, dish-washers. Delivered in natural and in the full RAL color scale. Modified copolymer PP, retarded with halogen flame retardant. Meets the basic electrotechnical properties: flammability in accordance with UL 94 V0 and 960°C glow wire.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.0237 cm/cm | 0.0237 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0233 cm/cm | 0.0233 in/in | STN 64 0808 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | STN EN ISO 527-2 |
| Elongation at Break | 30 % | 30 % | STN EN ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | STN EN ISO 527-2 |
| Flexural Strength | 35.0 MPa | 5080 psi | STN EN ISO 178 |
| Flexural Modulus | 1.00 GPa | 145 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -20.0 °C |
42.8 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 °C | 302 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | STN EN ISO 75/A |
| Vicat Softening Point | 105 °C | 221 °F | B; STN EN ISO 306 |
| Flammability, UL94 | V-2 | V-2 | |
| Glow Wire Test | 960 °C | 1760 °F | STN IEC 60695-2-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | STN IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | STN IEC 60093 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | STN IEC 60243 |
| Comparative Tracking Index | 450 V | 450 V | STN 34 6468 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Injection Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi |