Plastcom SLOVALEN PQ 51 N Polypropylene Homopolymer, Modified with Elastomer, Impacted
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVALEN PQ 51 N Polypropylene Homopolymer, Modified with Elastomer, Impacted.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FeaturesHomopolymer PP modified with elastomer. The addition of thermoplastic elastomer causes increased toughness, possible alternative to PP copolymers. General application in all industry branches - packing material, garden flower-pots, toys, furniture industry, hinges, fasteners, clamps, office chairs, hangers etc. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.880 g/cc | 0.0318 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0183 cm/cm | 0.0183 in/in | STN 64 0808 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | STN EN ISO 527-2 |
| Elongation at Break | 200 % | 200 % | STN EN ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | STN EN ISO 527-2 |
| Flexural Strength | 25.0 MPa | 3630 psi | STN EN ISO 178 |
| Flexural Modulus | 0.900 GPa | 131 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -20.0 °C |
23.8 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 140 °C | 284 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | STN EN ISO 75/A |
| Vicat Softening Point | 125 °C | 257 °F | B; STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Injection Pressure | 60.0 - 70.0 MPa | 8700 - 10200 psi |