Plastcom SLOVAMID® 6 GF 40 HI PA6 reinforced with glass fiber, improved impact strength

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade
Manufacturer	Plastcom spol. s r.o.
Trade Name	SLOVAMID®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom SLOVAMID® 6 GF 40 HI PA6 reinforced with glass fiber, improved impact strength.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PA 6 for injection molding, reinforced with 40% glass fiber, impact modified. Application: impacted moldings and moldings with higher strength applied in automotive, electrical, engineering and consumer-goods industry Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	STN EN ISO 1183-1
Filler Content	40 %	40 %
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	STN EN ISO 294-4
Linear Mold Shrinkage, Transverse	0.012 cm/cm	0.012 in/in	STN EN ISO 294-4
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 230 °C	1.0 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	160 MPa	23200 psi	STN EN ISO 527-2
Elongation at Break	3.0 %	3.0 %	STN EN ISO 527-2
Tensile Modulus	11.5 GPa	1670 ksi	STN EN ISO 527-2
Flexural Strength	245 MPa	35500 psi	STN EN ISO 178
Flexural Modulus	9.60 GPa	1390 ksi	STN EN ISO 178
Charpy Impact Unnotched	10.0 J/cm² @Temperature -20.0 °C	47.6 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	10.5 J/cm² @Temperature 23.0 °C	50.0 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179
Charpy Impact, Notched	1.40 J/cm² @Temperature -20.0 °C	6.66 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	2.50 J/cm² @Temperature 23.0 °C	11.9 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi)	205 °C	401 °F	STN EN ISO 75-2 (A)
Vicat Softening Point	205 °C	401 °F	STN EN ISO 306
Flammability, UL94	HB	HB
Glow Wire Test	650 °C @Thickness 3.00 mm	1200 °F @Thickness 0.118 in	STN EN 60695-2-12

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 270 °C	482 - 518 °F
Mold Temperature	70.0 - 90.0 °C	158 - 194 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.15 %	0.15 %	STN EN ISO 3344
Injection Pressure	70.0 - 120 MPa	10200 - 17400 psi