Plastcom SLOVAMID® 66 GF 20 HTS PA6 reinforced with glass fiber, heat stabilized, hydrolysis resistant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID® 66 GF 20 HTS PA6 reinforced with glass fiber, heat stabilized, hydrolysis resistant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA66 for injection molding, reinforced with 20% glass fiber, heat stabilized, hydrolysis resistant, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, gears, covers of electric tools, automobile mirror housings, cooling screws of blowers, electromotors, bearing parts in the automotive industry. Delivered in black color and in natural form.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
STN EN ISO 1183-1
Filler Content 20 %
20 %
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
STN EN ISO 294-4
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 275 °C
10 g/10 min

@Load 4.76 lb,
Temperature 527 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
STN EN ISO 527-2
Elongation at Break 3.5 %
3.5 %
STN EN ISO 527-2
Tensile Modulus 5.50 GPa
798 ksi
STN EN ISO 527-2
Flexural Strength 205 MPa
29700 psi
STN EN ISO 178
Flexural Modulus 4.70 GPa
682 ksi
STN EN ISO 178
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -20.0 °C
16.7 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.300 J/cm²

@Temperature -20.0 °C
1.43 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 250 °C
482 °F
STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 650 °C

@Thickness 3.00 mm
1200 °F

@Thickness 0.118 in
STN EN 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 250 - 290 °C
482 - 554 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 90.0 °C

@Time 14400 sec
194 °F

@Time 4.00 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 3344
Injection Pressure 80.0 - 110 MPa
11600 - 16000 psi
Descriptive Properties Value Comments
Color Black and Natural