Plastcom SLOVAMID® 6/6T GF 35 TS PA6/6T reinforced with glass fiber, improved heat resistance
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Partially Aromatic, Glass Filled , Nylon, Aromatic |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVAMID® 6/6T GF 35 TS PA6/6T reinforced with glass fiber, improved heat resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6/6T for injection molding, reinforced with 35% of glass fiber, for moldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry, improved heat resistance. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | STN EN ISO 1183-1 |
| Filler Content | 35 % | 35 % | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | STN EN ISO 294-4 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 275 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 527 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | STN EN ISO 527-2 |
| Elongation at Break | 2.0 % | 2.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 11.8 GPa | 1710 ksi | STN EN ISO 527-2 |
| Flexural Strength | 310 MPa | 45000 psi | STN EN ISO 178 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -20.0 °C |
42.8 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 295 °C | 563 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 275 °C | 527 °F | STN EN ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C @Thickness 3.00 mm |
1200 °F @Thickness 0.118 in |
STN EN 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+15 ohm-cm | 5.00e+15 ohm-cm | STN 34 6460 |
| Surface Resistance | 8.00e+13 ohm | 8.00e+13 ohm | STN 34 6460 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | STN EN 60243-2 |
| Comparative Tracking Index | 600 V | 600 V | STN EN 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 310 - 340 °C | 590 - 644 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi |