Plastcom SLOVASTER® B BT Polyethylene Terephthalate

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVASTER®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVASTER® B BT Polyethylene Terephthalate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPBT basic type for injection moulding. Melt is characterized by outstanding fluidity, which enables injection moulding of complicated and divided products also on multiple moulds. Anisotropy of shrinkage enables injection moulding of round, cylindrical or other hole products. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.018 cm/cm
0.018 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0193 cm/cm
0.0193 in/in
STN 64 0808
Melt Flow 40 g/10 min

@Load 2.16 kg,
Temperature 230 °C
40 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
STN EN ISO 527-2
Elongation at Break 8.0 %
8.0 %
STN EN ISO 527-2
Tensile Modulus 2.50 GPa
363 ksi
STN EN ISO 527-2
Flexural Strength 80.0 MPa
11600 psi
STN EN ISO 178
Flexural Modulus 2.50 GPa
363 ksi
STN EN ISO 178
Charpy Impact Unnotched 13.0 J/cm²

@Temperature 23.0 °C
61.9 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
13.0 J/cm²

@Temperature -20.0 °C
61.9 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
Charpy Impact, Notched 0.160 J/cm²

@Temperature 23.0 °C
0.761 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 200 - 220 °C
392 - 428 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
STN EN ISO 75/A
Vicat Softening Point 200 °C
392 °F
B; STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 850 °C
1560 °F
STN IEC 60695-2-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
STN IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
STN IEC 60093
Dielectric Strength 23.0 kV/mm
584 kV/in
STN IEC 60243
Comparative Tracking Index 600 V
600 V
STN 34 6468
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Drying Temperature 120 °C
248 °F
Dry Time 4 hour
4 hour
Moisture Content 0.050 %
0.050 %
STN EN ISO 960
Injection Pressure 60.0 - 100 MPa
8700 - 14500 psi