- Plastcom SLOVASTER® B GB 40 PBT reinforced with glass beads
Plastcom SLOVASTER® B GB 40 PBT reinforced with glass beads
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVASTER® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVASTER® B GB 40 PBT reinforced with glass beads.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT for injection molding, reinforced with 40% glass beads. Characterized by very good properties also at low temperature. Melt is characterized by very good rheology, which enables manufacturing of multiple products with complicated flow. Application in the automotive, electrical and engineering industry - connectors of cable harnesses, car-door locks, connection
links, grips etc. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | STN EN ISO 1183-1 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | STN EN ISO 294-4 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
15 g/10 min @Load 4.76 lb, Temperature 482 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | STN EN ISO 527-2 |
| Elongation at Break | 2.5 % | 2.5 % | STN EN ISO 527-2 |
| Tensile Modulus | 6.30 GPa | 914 ksi | STN EN ISO 527-2 |
| Flexural Strength | 110 MPa | 16000 psi | STN EN ISO 178 |
| Flexural Modulus | 5.10 GPa | 740 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 4.20 J/cm² @Temperature -20.0 °C |
20.0 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 228 °C | 442 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 245 °C | 473 °F | STN EN ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C @Thickness 3.00 mm |
1200 °F @Thickness 0.118 in |
STN EN 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | STN 34 6460 |
| Surface Resistance | 3.00e+16 ohm | 3.00e+16 ohm | STN 34 6460 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | STN EN 60243-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 100 °C @Time 7200 sec |
212 °F @Time 2.00 hour |
|
| Moisture Content | 0.10 % | 0.10 % | STN EN ISO 3344 |
| Injection Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi |