Plastics Group Polifil® GFRMPPCC-20 20% Glass Reinforced Polypropylene, High Impact

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler
Manufacturer The Plastics Group of America
Trade Name Polifil®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastics Group Polifil® GFRMPPCC-20 20% Glass Reinforced Polypropylene, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Applications: AppliancesElectrical componentsAutomotiveUtility products Standard processing techniques are applicable. Information provided by The Plastics Group.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Filler Content 20 %
20 %
ASTM D2584
Linear Mold Shrinkage 0.0040 cm/cm

@Thickness 1.59 mm
0.0040 in/in

@Thickness 0.0625 in
ASTM D955
Melt Flow 5.0 - 10 g/10 min
5.0 - 10 g/10 min
230/2.16; May be specified; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.8 MPa
8100 psi
ASTM D638
Elongation at Break 5.0 %
5.0 %
ASTM D638
Flexural Strength 64.1 MPa
9300 psi
ASTM D638
Flexural Modulus 2.90 GPa
420 ksi
Tangent; ASTM D790
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
At 73°F; ASTM D256
Gardner Impact 1.13 J
0.833 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 143 °C
290 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
260 °F
ASTM D648