Plenco 204 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Woodflour/Mineral Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 204 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok 204 is a two-stage, woodflour and mineral-filled phenolic molding compound formulated to accommodate a wide range of molding situations. In addition, it is recommended for use in thin wall applications where a UL94 V0 rating is required. This compound has been specially formulated in order to have improved electrical properties, as well as good machinability.Data provided by Plaslok Corporation.Plaslok Corporation was purchased by Plastics Engineering Company in March 2000. The Plaslok name is no longer used on any products.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
Apparent Bulk Density 0.600 g/cc
0.0217 lb/in³
ASTM D1895
Water Absorption 0.50 %
0.50 %
ASTM D570
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Compression; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Flexural Yield Strength 83.0 MPa
12000 psi
ASTM D790
Flexural Modulus 6.90 GPa
1000 ksi
ASTM D790
Compressive Yield Strength 207 MPa
30000 psi
ASTM D695
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
Flammability, UL94 V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
Oxygen Index 31.4 %
31.4 %
ASTM D2863
Electrical Properties Metric English Comments
Electrical Resistivity 1.80e+11 ohm-cm
1.80e+11 ohm-cm
ASTM D257
Dielectric Constant 5.2

@Frequency 1e+6 Hz
5.2

@Frequency 1e+6 Hz
ASTM D150
7.0

@Frequency 60 Hz
7.0

@Frequency 60 Hz
ASTM D150
Dielectric Strength 12.8 kV/mm
325 kV/in
ASTM D149
Dissipation Factor 0.030

@Frequency 1e+6 Hz
0.030

@Frequency 1e+6 Hz
ASTM D150
0.070

@Frequency 60 Hz
0.070

@Frequency 60 Hz
ASTM D150
Comparative Tracking Index 185 V
185 V
UL 746