Plenco 501 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Electrical Grade, Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 501 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok 501 is a two-stage, mineral and flock-filled phenolic molding compound designed for use in heat resistant and electrical applications. It is designed for elevated temperature exposure for extended periods of time. It exhibits good dimensional stability and flame resistance.Data provided by Plaslok Corporation.Plaslok Corporation was purchased by Plastics Engineering Company in March 2000. The Plaslok name is no longer used on any products.
Physical Properties Metric English Comments
Density 1.71 g/cc
0.0618 lb/in³
ASTM D792
Apparent Bulk Density 0.700 g/cc
0.0253 lb/in³
ASTM D1895
Water Absorption 0.20 %
0.20 %
ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Compression; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Flexural Yield Strength 76.0 MPa
11000 psi
ASTM D790
Flexural Modulus 9.00 GPa
1310 ksi
ASTM D790
Compressive Yield Strength 221 MPa
32100 psi
ASTM D695
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 177 °C
351 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
Flammability, UL94 V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 4.8

@Frequency 1e+6 Hz
4.8

@Frequency 1e+6 Hz
ASTM D150
6.5

@Frequency 60 Hz
6.5

@Frequency 60 Hz
ASTM D150
Dielectric Strength 13.0 kV/mm
330 kV/in
ASTM D149
Dissipation Factor 0.030

@Frequency 1e+6 Hz
0.030

@Frequency 1e+6 Hz
ASTM D150
0.12

@Frequency 60 Hz
0.12

@Frequency 60 Hz
ASTM D150
Comparative Tracking Index 160 V
160 V
UL 746