Plenco 50130 PET, Pellet, Injection Molded, Natural Color  (discontinued **)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 50130 PET, Pellet, Injection Molded, Natural Color  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PLENCO 50130 is an engineering grade glass reinforced UL flame rated polyethylene terephthalate resin designed for good physical strength. It is UL listed and available in natural and black.Information supplied by PlencoPlenco discontinued their PET product line in 2005.
Physical Properties Metric English Comments
Density 1.72 g/cc
0.0621 lb/in³
ASTM D792
Water Absorption 0.070 %
0.070 %
ASTM D570
Linear Mold Shrinkage 0.00090 cm/cm
0.00090 in/in
ATM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 136.6 MPa
19810 psi
ASTM D638
Elongation at Break 1.58 %
1.58 %
ASTM D638
Tensile Modulus 10.92 GPa
1584 ksi
ASTM D638
Flexural Yield Strength 214.5 MPa
31110 psi
ASTM D790
Flexural Modulus 10.76 GPa
1561 ksi
ASTM D790
Compressive Yield Strength 173.1 MPa
25110 psi
ASTM D695
Izod Impact, Notched 0.720 J/cm
1.35 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 224 °C
435 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0579 in
Oxygen Index 31 %
31 %
ASTM D2863
Electrical Properties Metric English Comments
Electrical Resistivity 3.5307e+16 ohm-cm
3.5307e+16 ohm-cm
ASTM D257
Dielectric Constant 3.1

@Frequency 1e+6 Hz
3.1

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm
483 kV/in
Short Time; ASTM D149
Dissipation Factor 0.012

@Frequency 1e+6 Hz
0.012

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 30 sec
30 sec
ASTM D495
Comparative Tracking Index 200 V
200 V
ASTM D3638