Plenco 5303 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Electrical Grade, Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 5303 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok 5303 is a two-stage, mineral and flock-filled phenolic molding compound designed for use in appliance, automotive and electrical applications. It can be molded by compression, transfer or injection processes.Data provided by Plaslok Corporation.Plaslok Corporation was purchased by Plastics Engineering Company in March 2000. The Plaslok name is no longer used on any products.
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
ASTM D792
Apparent Bulk Density 0.650 g/cc
0.0235 lb/in³
ASTM D1895
Water Absorption 0.18 %
0.18 %
ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Compression; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Flexural Yield Strength 69.0 MPa
10000 psi
ASTM D790
Flexural Modulus 9.70 GPa
1410 ksi
ASTM D790
Compressive Yield Strength 206 MPa
29900 psi
ASTM D695
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 182 °C
360 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
Flammability, UL94 V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
Oxygen Index 31.4 %
31.4 %
ASTM D2863
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 4.8

@Frequency 1e+6 Hz
4.8

@Frequency 1e+6 Hz
ASTM D150
8.0

@Frequency 60 Hz
8.0

@Frequency 60 Hz
ASTM D150
Dielectric Strength 14.8 kV/mm
376 kV/in
ASTM D149
Dissipation Factor 0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
ASTM D150
0.15

@Frequency 60 Hz
0.15

@Frequency 60 Hz
ASTM D150
Comparative Tracking Index 185 V
185 V
UL 746