Polimeri Europa Clearflex® CL D0 Very Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Very Low Density Polyethylene (VLDPE)
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® CL D0 Very Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex CL D0 is a linear low density polyethylene, with antioxidants, characterized by a very low density (VLDPE).This resin is produced with a proprietary technology. Stretch films manufactured with Clearflex CL D0 have high stretchability, outstanding clarity and a very high constancy in cling effect.Main Applications: Clearflex CL D0 is recommended as a cling agent in stretch film but is also used for applications in which soft touch and flexibility are required, for the improvement of impact resistance when used as additive in blend with other polyolefins formulated with or without mineral fillers.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.900 g/cc
0.900 g/cc
ISO 1183
Thickness 8.00 - 50.0 microns
0.315 - 1.97 mil
Recommended
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 5.00 MPa
725 psi
ISO 527-3
Film Tensile Strength at Yield, TD 5.00 MPa
725 psi
ISO 527-3
Film Elongation at Break, MD 600 %
600 %
ISO 527-3
Film Elongation at Break, TD 800 %
800 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 4.076 g/micron
103.5 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 8.3558 g/micron
212.24 g/mil
ISO 6383-2
Dart Drop Test 210 g
0.463 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 31.0 MPa
4500 psi
ISO 527-3
Film Tensile Strength at Break, TD 26.0 MPa
3770 psi
ISO 527-3
1% Secant Modulus, MD 40.0 MPa
5800 psi
ISO 527-3
1% Secant Modulus, TD 50.0 MPa
7250 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 115 °C
239 °F
Internal method
Vicat Softening Point 54.0 °C

@Load 1.00 kg
129 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 1.5 %
1.5 %
ISO 14782
Gloss 84 %
84 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified