Polimeri Europa EDISTIR PD RK4514H High Impact Polystyrene (HIPS) (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa EDISTIR PD RK4514H High Impact Polystyrene (HIPS)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: S/B Designation: Thermoplastic ISO 2897-SB,M,093-06-07-23 UL94 V-2, polybromodiphenylether (PBBE) free, antimony free, HIPS satisfying at 960°C the glow wire test (GWT) acc. DIN/IEC 695-2-1. This product is suggested for injection molding where exhibits good flow, good mechanical and thermal properties and enhanced UV stability. Applications: Developed for fuse and circuit breaker boxes, cable junction boxes and other electrical appliances.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50 mm/min |
| Elongation at Break | 40 % | 40 % | Nominal |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | |
| 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 92.0 °C | 198 °F | 50°C/hr; 50N |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| Dielectric Strength | 65.0 kV/mm | 1650 kV/in | |
| Dissipation Factor | 0.00060 @Frequency 100 Hz |
0.00060 @Frequency 100 Hz |
|
| Comparative Tracking Index | 475 V | 475 V |