Polimeri Europa Edistir R 540E Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Edistir
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Edistir R 540E Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HIPS with high stiffness, matt surface finish and good heat resistance. Suitable for general extrusion of thick sheets and profiles. Also used for injection moldings. Designation: Thermoplastics ISO 2897-PS-I,G,093-03-07-18Applications: To be used in industrial panels for appliances and buildings. Injection molding of shoe heels.R 540E satisfies UL94 HB at 1.5 mm (internal test). This grade in natural version complies by composition with the requirements set by the main Regulations for plastic materials intended for food contact (included the EEC Directive 90/128 and following amendments).Information provided by Polimeri Europa
Physical Properties Metric English Comments
Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
24 hours - 23°C; ISO 62
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Internal Method
Melt Flow 4.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
4.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell L 70
70
ISO 2039/2
Tensile Strength at Break 29.0 MPa
4210 psi
50 mm/min; ISO 527
Tensile Strength, Yield 24.0 MPa
3480 psi
50 mm/min; ISO 527
Elongation at Break 60 %
60 %
50 mm/min; ISO 527
Tensile Modulus 2.00 GPa
290 ksi
1 mm/min; ISO 527
Flexural Strength 43.0 MPa
6240 psi
2 mm/min; ISO 178
Izod Impact, Notched 1.00 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.87 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ISO 180/4A
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Thickness 4.00 mm,
Temperature -30.0 °C
2.86 ft-lb/in²

@Thickness 0.157 in,
Temperature -22.0 °F
ISO 180/1A
8.00 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
3.81 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
120°C/h; ASTM D 648
Vicat Softening Point 92.0 °C
198 °F
50 N - 50°C/h; ISO 306/B
100 °C
212 °F
10 N - 50°C/h; ISO 306/A
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+15 ohm-cm
7.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.50e+15 ohm
1.50e+15 ohm
IEC 60093
Dielectric Constant 2.5

@Frequency 50 Hz
2.5

@Frequency 50 Hz
IEC 60250
Dielectric Strength 65.0 kV/mm
1650 kV/in
IEC 60243
Dissipation Factor 0.00030

@Frequency 50 Hz
0.00030

@Frequency 50 Hz
IEC 60250
Comparative Tracking Index 500 V
500 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 210 - 240 °C
410 - 464 °F
Extrusion
210 - 260 °C
410 - 500 °F
Injection Molding
Mold Temperature 20.0 - 60.0 °C
68.0 - 140 °F
Injection Molding