Polimeri Europa Eraclene® BC 86 High Density Polyethylene - Blow Molding

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Eraclene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Eraclene® BC 86 High Density Polyethylene - Blow Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Eraclene BC 86 is a high density polyethylene resin (HDPE) with antioxidants, suitable for blow molding application. It is especially recommended for the production of containers up to 20 liters.Eraclene BC 86 combines a excellent stress cracking resistance with a good rigidity and high impact strength. This resin is characterized by a broad molecular weight distribution which balances overall performances with ease of processing.Main Applications: Eraclene BC 86 is used to produce blow molded containers to package household and industrial chemicals (detergents, perfumed bleaches, softener), cosmetics (shampoos, creams, lotions, etc), health and medical aids, fertilizers, adhesives and pesticides. Eraclene BC 86 can be extruded into profiles and sheets.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.953 g/cc
0.953 g/cc
ISO 1183
Environmental Stress Crack Resistance >= 500 hour
>= 500 hour
ISO 22088
Melt Flow 0.20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
0.80 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.80 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
21 g/10 min

@Load 21.6 kg,
Temperature 190 °C
21 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 64
64
ISO 868/A
Tensile Strength at Break 30.0 MPa
4350 psi
ISO 527
Tensile Strength, Yield 27.0 MPa
3920 psi
ISO 527
Elongation at Break >= 600 %
>= 600 %
ISO 527
Flexural Modulus 1.20 GPa
174 ksi
ISO 178
Izod Impact, Notched 1.80 J/cm
3.37 ft-lb/in
ISO 180/A
Thermal Properties Metric English Comments
Melting Point 135 °C
275 °F
Internal method
Vicat Softening Point 125 °C

@Load 1.00 kg
257 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -60.0 °C
<= -76.0 °F
ASTM D746