Polimeri Europa Eraclene® FC 82 High Density Polyethylene - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Eraclene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Eraclene® FC 82 High Density Polyethylene - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Eraclene FC 82 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high film strength.Main Applications: Films produced with Eraclene FC 82 are recommended for high strength grocery sacks, shopping bags, notion and millinery bags. The excellent balance between drawability and bubble stability make Eraclene FC 82 perfect for manufacturing of high strength thin films (shopping bags, bags on the reel, lamination film).Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.953 g/cc
0.953 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
23 g/10 min

@Load 21.6 kg,
Temperature 190 °C
23 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ISO 527-3
Film Elongation at Break, TD 650 %
650 %
ISO 527-3
Elmendorf Tear Strength, MD 1.019 g/micron
25.88 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 2.5475 g/micron
64.706 g/mil
ISO 6383-2
Dart Drop Test 70.0 g
0.154 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ISO 527-3
Film Tensile Strength at Break, TD 45.0 MPa
6530 psi
ISO 527-3
1% Secant Modulus, MD 650 MPa
94300 psi
ISO 527-3
1% Secant Modulus, TD 800 MPa
116000 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 135 °C
275 °F
Internal method
Vicat Softening Point 127 °C

@Load 1.00 kg
261 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -60.0 °C
<= -76.0 °F
ASTM D746