Polimeri Europa Greenflex® FF 55 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Greenflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Greenflex® FF 55 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Greenflex FF 55 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FF 55 show high flexibility.Main Applications: Greenflex FF 55 is recommended for the production of greenhouse film and flexible packaging, especially where high fracture mechanical properties (impact resistance) are required.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.941 g/cc
0.941 g/cc
ISO 1183
Vinyl Acetate Content 19 %
19 %
Internal Method
Thickness 30.0 - 150 microns
1.18 - 5.91 mil
Recommended
Melt Flow 0.70 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.70 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 89
89
ISO 868/A
Hardness, Shore D 38
38
ISO 868/A
Film Tensile Strength at Yield, MD 4.00 MPa
580 psi
ISO 527-3
Film Tensile Strength at Yield, TD 4.00 MPa
580 psi
ISO 527-3
Film Elongation at Break, MD 500 %
500 %
ISO 527-3
Film Elongation at Break, TD 700 %
700 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 3.3627 g/micron
85.413 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 5.6045 g/micron
142.35 g/mil
ISO 6383-2
Dart Drop Test >= 700 g
>= 1.54 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 36.0 MPa
5220 psi
ISO 527-3
Film Tensile Strength at Break, TD 34.0 MPa
4930 psi
ISO 527-3
1% Secant Modulus, MD 42.0 MPa
6090 psi
ISO 527-3
1% Secant Modulus, TD 45.0 MPa
6530 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 84.0 °C
183 °F
Internal Method
Vicat Softening Point 60.0 °C

@Load 1.00 kg
140 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -80.0 °C
<= -112 °F
ASTM D746
Optical Properties Metric English Comments
Haze 1.0 %
1.0 %
ISO 14782
Gloss 87 %
87 %
45°; ASTM D2457