Polimeri Europa KOBLEND HI PD 14 PBT+PC, Impact Grade  (discontinued **)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa KOBLEND HI PD 14 PBT+PC, Impact Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified PBT+PC blend, similar to KOBLEND HI 18 with higher shrinkage values. Main application fields: bumpersUnfilled. Suitable for Injection Molding. Supplied as pellets.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Melt Flow 2.2 g/10 min

@Load 2.16 kg,
Temperature 250 °C
2.2 g/10 min

@Load 4.76 lb,
Temperature 482 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 MPa
5220 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal
Elongation at Yield 3.9 %
3.9 %
50 mm/min
Tensile Modulus 1.70 GPa
247 ksi
1 mm/min
Izod Impact, Unnotched NB
NB
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Izod Impact, Notched (ISO) 65.0 kJ/m²

@Temperature -30.0 °C
30.9 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 113 °C
235 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Comparative Tracking Index 500 V
500 V