Polimeri Europa KOBLEND PCA 447F PC+ABS (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa KOBLEND PCA 447F PC+ABS
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043/1: PC+ABS Similar to KOBLEND PCA 447 with improved fluidity and release, suitable to mould complex items.Unfilled. Suitable for Injection Molding. Supplied as pellets.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | |
| Water Absorption | 0.70 % | 0.70 % | |
| Melt Flow | 18 g/10 min @Load 5.00 kg, Temperature 260 °C |
18 g/10 min @Load 11.0 lb, Temperature 500 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min |
| Izod Impact, Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Izod Impact, Notched (ISO) | 22.0 kJ/m² @Temperature -30.0 °C |
10.5 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | |
| Vicat Softening Point | 113 °C | 235 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.7 @Frequency 1e+6 Hz |
2.7 @Frequency 1e+6 Hz |
|
| 2.8 @Frequency 100 Hz |
2.8 @Frequency 100 Hz |
||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | |
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
|
| 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 500 V | 500 V |