Polimeri Europa Riblene® FC 40 Low Density Polyethylene - Blown Film Extrusion

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Polimeri Europa (Former EniChem)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa Riblene® FC 40 Low Density Polyethylene - Blown Film Extrusion.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Riblene FC 40 is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 40 is characterized by a high melt strength leading to a good bubble stability during extrusion.Films manufactured with Riblene FC 40 are easily heat shrinkable and characterized by high rigidity, good mechanical and excellent optical properties.Main Applications: Riblene FC 40 is recommended for the production of shrink film for medium and high loads characterized by high rigidity, clarity and gloss.Information provided by Polimeri Europa.

Physical Properties	Metric	English	Comments
Specific Gravity	0.928 g/cc	0.928 g/cc	ISO 1183
Thickness	40.0 - 150 microns	1.57 - 5.91 mil	Recommended
Melt Flow	0.27 g/10 min @Load 2.16 kg, Temperature 190 °C	0.27 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	12.0 MPa	1740 psi	ISO 527-3
Film Tensile Strength at Yield, TD	12.0 MPa	1740 psi	ISO 527-3
Film Elongation at Break, MD	550 %	550 %	ISO 527-3
Film Elongation at Break, TD	650 %	650 %	ISO 527-3
Coefficient of Friction, Dynamic	>= 0.50	>= 0.50	ISO 8295
Elmendorf Tear Strength, MD	3.5665 g/micron	90.589 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	5.095 g/micron	129.4 g/mil	ISO 6383-2
Dart Drop Test	300 g	0.662 lb	F50; ISO 7765-1
Film Tensile Strength at Break, MD	28.0 MPa	4060 psi	ISO 527-3
Film Tensile Strength at Break, TD	28.0 MPa	4060 psi	ISO 527-3
1% Secant Modulus, MD	230 MPa	33400 psi	ISO 527-3
1% Secant Modulus, TD	240 MPa	34800 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	116 °C	241 °F	Internal method
Vicat Softening Point	93.0 °C @Load 1.00 kg	199 °F @Load 2.20 lb	ISO 306/A
Brittleness Temperature	<= -75.0 °C	<= -103 °F	ASTM D746

Optical Properties	Metric	English	Comments
Haze	6.5 %	6.5 %	ISO 14782
Gloss	70 %	70 %	45°; ASTM D2457