- Polimeri Europa Riblene® FH 10 Low Density Polyethylene - Blown Film Extrusion
Polimeri Europa Riblene® FH 10 Low Density Polyethylene - Blown Film Extrusion
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Polimeri Europa (Former EniChem) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa Riblene® FH 10 Low Density Polyethylene - Blown Film Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Riblene FH 10 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FH 10 is characterized by a good balance between processability and mechanical properties.Films manufactured with Riblene FH 10 are easily heat shrinkable and have good optical and mechanical properties.Main Applications: Riblene FH 10 is recommended for general blown film applications, for the production of packaging film and for blend.Information provided by Polimeri Europa.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ISO 1183 |
| Thickness | 30.0 - 100 microns | 1.18 - 3.94 mil | Recommended |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 5.095 g/micron | 129.4 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 5.095 g/micron | 129.4 g/mil | ISO 6383-2 |
| Dart Drop Test | 240 g | 0.529 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 160 MPa | 23200 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 180 MPa | 26100 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | Internal method |
| Vicat Softening Point | 90.0 °C @Load 1.00 kg |
194 °F @Load 2.20 lb |
ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.5 % | 8.5 % | ISO 14782 |
| Gloss | 63 % | 63 % | 45°; ASTM D2457 |