Polimeri Europa SINKRAL B260 ABS, Heat Stabilized  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa SINKRAL B260 ABS, Heat Stabilized  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,115-04-09-25 Very high heat injection moulding grade with good impact resistance for this category of ABS. Mainly used for automotive interior (dashboard inserts) and exterior (painted wheel covers) applications.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
Water Absorption 1.0 %
1.0 %
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption
Melt Flow 2.5 g/10 min

@Load 10.0 kg,
Temperature 220 °C
2.5 g/10 min

@Load 22.0 lb,
Temperature 428 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Yield 48.0 MPa
6960 psi
50 mm/min
Elongation at Break 15 %
15 %
Nominal
Elongation at Yield 3.5 %
3.5 %
50 mm/min
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min
Charpy Impact Unnotched 12.0 J/cm²
57.1 ft-lb/in²
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 107 °C
225 °F
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Vicat Softening Point 113 °C
235 °F
50°C/hr; 50N
Glass Transition Temp, Tg 127 °C
261 °F
10°C/min test
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
Dielectric Strength 30.0 kV/mm
762 kV/in
Dissipation Factor 0.0050

@Frequency 1e+6 Hz
0.0050

@Frequency 1e+6 Hz
0.0060

@Frequency 100 Hz
0.0060

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V