Polimeri Europa SINKRAL D160 ABS, Heat Stabilized (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa SINKRAL D160 ABS, Heat Stabilized
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,115-08-09-25 Very high heat injection moulding grade with good flow. Permits production of complex, thin walled items. SINKRAL D160 is typically used in the automotive sector for interior and exterior parts such as wheel covers (painted), dashboard inserts, air grilles and rear lamp housings (vacuum metal plated).Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Water Absorption | 1.0 % | 1.0 % | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Humidity Absorption |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min |
| Elongation at Break | 15 % | 15 % | Nominal |
| Elongation at Yield | 3.1 % | 3.1 % | 50 mm/min |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | |
| Vicat Softening Point | 113 °C | 235 °F | 50°C/hr; 50N |
| Glass Transition Temp, Tg | 126 °C | 259 °F | 10°C/min test |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
|
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 1e+6 Hz |
0.0050 @Frequency 1e+6 Hz |
|
| 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |