Polimeri Europa SINKRAL D720 ABS, Impact Grade  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa SINKRAL D720 ABS, Impact Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-08-35-15 High impact injection moulding grade, with improved flow compared with SINKRAL B620 and a high gloss. Can be used to mould of helmets as well as in compounds with SAN for the production of 'tailored' ABS grades.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Water Absorption 1.0 %
1.0 %
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Yield 34.0 MPa
4930 psi
50 mm/min
Elongation at Break 20 %
20 %
Nominal
Elongation at Yield 3.5 %
3.5 %
50 mm/min
Tensile Modulus 1.70 GPa
247 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Charpy Impact, Notched 3.00 J/cm²
14.3 ft-lb/in²
1.90 J/cm²

@Temperature -30.0 °C
9.04 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
Vicat Softening Point 94.0 °C
201 °F
50°C/hr; 50N
Glass Transition Temp, Tg 105 °C
221 °F
10°C/min test
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.7

@Frequency 100 Hz
2.7

@Frequency 100 Hz
3.1

@Frequency 1e+6 Hz
3.1

@Frequency 1e+6 Hz
Dielectric Strength 30.0 kV/mm
762 kV/in
Dissipation Factor 0.0065

@Frequency 1e+6 Hz
0.0065

@Frequency 1e+6 Hz
0.0090

@Frequency 100 Hz
0.0090

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V