Polimeri Europa Sinkral® PD D 232/M4 ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Polimeri Europa (Former EniChem) |
| Trade Name | Sinkral® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa Sinkral® PD D 232/M4 ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Special very low gloss extrusion / co-extrusion grade, with good flow.Applications: Sinkral PD D 232/M4 is widely used in extrusion / co-extrusion of foils, when a very high matte appearance is required, as well as in the extrusion of profiles.Information provided by Polimeri Europa.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ISO 1183 |
| Water Absorption | 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
ASTM D570 |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ISO 2039/2 |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 1.55 GPa | 225 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
1.41 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ISO 180/4A |
| 0.800 J/cm @Thickness 3.20 mm, Temperature -20.0 °C |
1.50 ft-lb/in @Thickness 0.126 in, Temperature -4.00 °F |
ISO 180/4A | |
| 0.900 J/cm @Thickness 3.20 mm, Temperature 0.000 °C |
1.69 ft-lb/in @Thickness 0.126 in, Temperature 32.0 °F |
ISO 180/4A | |
| 1.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ISO 180/4A | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Thickness 4.00 mm, Temperature -40.0 °C |
3.33 ft-lb/in² @Thickness 0.157 in, Temperature -40.0 °F |
ISO 180/1A |
| 9.50 kJ/m² @Thickness 4.00 mm, Temperature 23.0 °C |
4.52 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
DIN 53453 |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | ASTM C177 |
| Vicat Softening Point | 101 °C @Load 5.10 kg |
214 °F @Load 11.2 lb |
ISO 306/B 120 |
| 106 °C @Load 1.02 kg |
223 °F @Load 2.25 lb |
ISO 306/A 120 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| Glow Wire Test | 650 °C @Thickness 3.00 mm |
1200 °F @Thickness 0.118 in |
IEC 60695-2-1 |
| Shrinkage | 0.40 - 0.60 % | 0.40 - 0.60 % | Internal method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1000 Hz |
3.1 @Frequency 1000 Hz |
dry; IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.015 @Frequency 1000 Hz |
0.015 @Frequency 1000 Hz |
dry; IEC 60250 |