PolyOne Edgetek® AS-1000 Acrylonitrile Butadiene Styrene (ABS) (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-1000 Acrylonitrile Butadiene Styrene (ABS)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:UnfilledPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Ultimate | 42.1 MPa | 6100 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.4 °C | 211 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.4 °C | 202 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 227 - 249 °C | 440 - 480 °F | Molding |
| Mold Temperature | 26.7 - 60.0 °C | 80.0 - 140 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Radici Radilon® A USZ200 (cond.) Nylon 66
- Greene Tweed Arlon® 1330 PEEK
- Michelman® VaporCoat® 330C Topical MVTR
- Saint-Gobain COHRlastic® 100S Silicone Sponge/High Temp Silicone Adhesive Pressure Sensitive Tape
- Tipco Tipcolene® DR 8201 - 20% Talc/Mineral Reinforced, Impact Modified, Polypropylene Copolymer
- A. Schulman POLYBATCH™ Ivory 90033/4 Concentrate Based In LDPE
- Hexcel® HexPly® F155 Epoxy Resin, T2C190 Carbon Tape
- Ensinger Tecatron® XP-85 Compression Molded PPS Compound, with 30% Carbon Fiber
- DuPont Performance Polymers Neoprene SW Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved