- PolyOne Edgetek® AT-5GB/000 Acetal-Copolymer, Glass Bead Filled (discontinued **)
PolyOne Edgetek® AT-5GB/000 Acetal-Copolymer, Glass Bead Filled (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AT-5GB/000 Acetal-Copolymer, Glass Bead Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.432 g/cc | 1.432 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Thickness 3.17 mm |
0.10 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 12 % | 12 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 216 °C | 370 - 420 °F | Molding |
| Mold Temperature | 54.4 - 76.7 °C | 130 - 170 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL® 6510 Conductive Elastomer
- Formosa Plastics Formolene® LH5326 Injection Molding HDPE (discontinued **)
- 3M Dyneon™ TF 5235 PTFE Dispersion (discontinued **)
- Momentive Performance Materials RTV5223 Neutral Cure, One Component RTV Adhesive Sealant
- Teknor Apex APEX® 1519-39 Polyvinyl Chloride, Flexible
- Chesterton OPTICOOL™ 462 Lubrication
- Covestro Apec® HT KU 1-9371 High-Heat Polycarbonate
- Colorite Polymers CS9034SR Wire and Cable Insulation Vinyl Compound
- Axiall 22912 Coax & Telecom Flexible PVC
- ExxonMobil Santoprene® 101-60W261 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved