PolyOne Edgetek® NN-30GF/000 Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® NN-30GF/000 Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Water Absorption | 0.70 % @Thickness 0.508 mm |
0.70 % @Thickness 0.0200 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 8.27 GPa | 1200 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 290 MPa | 42100 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.18 mm |
486 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Flammability, UL94 | HB | HB | UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 277 - 299 °C | 531 - 570 °F | |
| Mold Temperature | 82.2 - 121 °C | 180 - 250 °F | |
| Drying Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| RoHS Compliance | RoHS Compliant |