PolyOne Edgetek® PK-20GF/000 Polyetheretherketone (PEEK), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PK-20GF/000 Polyetheretherketone (PEEK), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedUL 94 (CTI Testing)PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hr. Immersion, -; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 145 MPa | 21000 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 8.27 GPa | 1200 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 221 MPa | 32000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.60 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.9 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 382 - 393 °C | 720 - 740 °F | Molding |
| Mold Temperature | 149 °C | 300 °F | |
| Drying Temperature | 149 °C | 300 °F | 2 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- NeXolve LaRC™-CP1 Polyimide
- Garlock GYLON® 3522 PTFE Diaphragm
- Mi-Tech Metals TC50 50 Tungsten Carbide/50 Copper PM Metal Composite
- Gromax BFG30-FN00N1 Nylon 6 30% Glass Filled (Dry)
- Karina E 81-10/43-CR White PVC Compound
- Henkel Hysol EA 9258.1 Primer
- A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene
- A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide
- Azoty Tarnow™ Alphalon™ E 36 L Nylon 6
- Pacific Sintered Materials BT-126 Bronze Powdered Metal
Copyright © lookpolymers.com All Rights Reserved