- PolyOne Edgetek® RA-30CF/000 Polyarylsulfone, Carbon Fiber Reinforced (discontinued **)
PolyOne Edgetek® RA-30CF/000 Polyarylsulfone, Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyarylsulfone (PAS) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® RA-30CF/000 Polyarylsulfone, Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 193 MPa | 28000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 12.4 GPa | 1800 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 10 - 100 ohm | 10 - 100 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 - 382 °C | 650 - 720 °F | Molding |
| Mold Temperature | 93.3 - 149 °C | 200 - 300 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Eastman Eastalloy DA003 PC+PCTG Copolyester/Polycarbonate (discontinued **)
- Lucky IF-870 Acrylic, High Flow Grade
- Chase Plastics CP Pryme® N100L (DAM) Nylon 6, Internally Lubricated
- Unipetrol Raffinate II
- A. Schulman POLYBATCH™ Forest Green LL30318 Concentrate Based In LLDPE
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Fiber Reinforced, Heat Impact Nylon 6
- A. Schulman INVISION™ VX-5070UI Soft Touch Polyolefin Thermoplastic
- DuPont Performance Polymers Zytel® FG133F1 NC010 Nylon 66 (Unverified Data**)
- Esstech X-731-7046 Trifluoroethyl Methacrylate, C6H7O2F3
Copyright © lookpolymers.com All Rights Reserved