- PolyOne Edgetek® SF-20GF/000 Polyphenylene Sulfide (PPS), Glass Filled (discontinued **)
PolyOne Edgetek® SF-20GF/000 Polyphenylene Sulfide (PPS), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SF-20GF/000 Polyphenylene Sulfide (PPS), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 97.9 MPa | 14200 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 8.446 GPa | 1225 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 139.6 MPa | 20250 psi | ASTM D790 |
| Flexural Modulus | 7.412 GPa | 1075 ksi | ASTM D790 |
| Izod Impact, Notched | 0.635 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.19 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 28.8 µm/m-°C @Temperature 20.0 °C |
16.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
| Mold Temperature | 37.8 - 149 °C | 100 - 300 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 34-700 12K 2x2 Twill Reinforced
- Abatron 226 A/B Filled Potting Compound (discontinued **)
- Polykemi AB POLYabs F00 ABS
- Kazanorgsintez 158-76 Film Grade Composition of High Density Polyethylene
- Lucite International Elvacite ® 2669 Acrylic Resin
- Samsung Cheil Industries Starex® VE-1801 HIPS, Unreinforced FR
- SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Europe-Africa-Middle East)
- AorTech Biomaterials Elast-Eon™ E4 Biomedical Polyurethane Pellets
- Colorite Polymers 7011G-015 (Extrustion), 7012G-015 (Molding) Radiation Sterilizable Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved